Stainles Steel 430 Flanges

Stainless steel 430 flanges from 15NB (1/2”) to 600NB (24”) in Weld neck. Slip-on, Blind, Lap joint, Bossed, Socket Weld and Threaded according to the following standards are available.

As an acclaimed undertaking of the business, Calico Metal is included in offering an unfathomable cluster of Stainless Steel 430 Flanges as a maker, exporter, stockiest and supplier to our household and worldwide customers. Stainless Steel 347H is the low carbon rendition of 310. It doesn't require post-weld toughening as is widely utilized as a part of substantial gage segments (over around 6mm). Stainless Steel Grade 430 with its higher carbon content discovers application at elevated temperatures.

Regarding diverse evaluations, we offer these Flanges in various sorts, for example, SS Slip On Flanges, SS Blind Flanges, SS Weld Neck Flanges, SS Socket Weld Flanges, SS Spectacle Blind Flanges, SS Screwed/Threaded Flanges, SS Reducing Flanges, and SS Ring Type Joint Flanges (RTJ). In the interim, our costs of such spines are set remembering customers prerequisite.

430 is a molybdenum bearing, low carbon content "L" grade austenitic stainless steel that provides improved corrosion resistance over 304L and 316L stainless steels. The low carbon provides resistance to sensitization during welding and other thermal processes. 430 is non-magnetic in the annealed condition but may become slightly magnetic as a result of welding. 430 has excellent corrosion resistance in a wide range of chemicals, especially in acidic chloride environments such as those encountered in pulp and paper mills. Increased levels of chromium, nickel and molybdenum compared to 316L stainless steel improve resistance to chloride pitting and general corrosion.

430 has excellent corrosion resistance in a wide range of chemicals, especially in acidic chloride environments such as those encountered in pulp and paper mills. Increased levels of chromium, nickel and molybdenum compared to 316L stainless steel improve resistance to chloride pitting and general corrosion. Resistance increases with molybdenum alloy content. 347H is resistant to sulfuric acid concentrations up to 5 percent at temperatures as high as 120°F (49°C).

Applications

  • Aerospace – piston engine manifolds
  • Chemical Processing
  • Expansion Joints
  • Food Processing – equipment and storage
  • Petroleum Refining – polythionic acid service
  • Waste Treatment – thermal oxidizers

Chemical Composition

Grade C Mn Si P S Cr MO Ni CU
430 Min - - - - - 12.0 - - -
max 0.15 1.00 1.00 0.04 0.03 14.0 - - -

Mechanical Properties

Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness
Rockwell B (HR B) Brinell (HB)
430 95,000 50,000 25 - 175

Physical Properties

Grade Density (kg/m3) Elastic Modulus (GPa) Mean Coefficient of Thermal Expansion
(mm/m/°C)
Thermal Conductivity
(W/m.K)
Specific Heat 0-100°C (J/kg.K) Electrical Resistivity (nW.m)
SS 430 0-100°C 0-315°C 0-538°C at 100°C at 500°C
-7750 200 10.4 11.0 11.4 23.9 26.0 460 600

Calico Metal Ind Pvt Ltd exports their products to countries like UAE, Bahrain, Italy, Indonesia, Malaysia, United States, Mexico, Chine, Brazil, Peru, Nigeria, Kuwait, Jordan, Dubai, Thailand (Bangkok), Venezuela, Iran, Germany, UK, Canada, Russia, Turkey, Australia, New Zealand, Sri Lanka, Vietnam, South Africa, Kazakhstan & Saudi Arabia.